Impuphu ye-yttrium oxide engavamile yomhlaba 1314-36-9
Isingeniso esifushane se-Yttrium Oxide
Ifomula (Y2O3)
Inombolo ye-CAS: 1314-36-9
Ubumsulwa: 99.999%
I-SSA: 25-45 m2/g
Umbala: omhlophe
Ukwakheka: okuyisiyingi
Ubuningi: 0.31 g/cm3
Ubuningi Beqiniso: 5.01 g/cm3
Isisindo sama-molecule: 225.81
Iphuzu lokuncibilika: 2425 celsium degree
Ukubukeka: Impuphu emhlophe
Ukuncibilika: Akuncibiliki emanzini, kuncibilika ngokulingene kuma-asidi amaminerali aqinile
Ukuzinza: Kuncane kancane
Isicelo se-Yttrium Oxide
1: I-Yttrium Oxide, ebizwa nangokuthi i-Yttria, ubumsulwa obukhulu. Ama-Yttrium Oxides ayizinto ezibaluleke kakhulu zama-tri-bands ama-Rare Earth phosphors anikeza umbala obomvu kumabonakude ombala kanye namashubhu ekhompyutha.
2: Embonini yokukhanya, i-Yttrium Oxide isetshenziselwa ukukhiqiza ama-Yttrium-Iron-Garnets, okuyizihlungi ze-microwave ezisebenza kahle kakhulu.
3: Ubumsulwa obuphansi be-Yttrium Oxide busetshenziswa kabanzi ku-ceramics kagesi. Isetshenziswa kabanzi ukwenza ama-phosphor e-Eu:YVO4 kanye ne-Eu:Y2O3 anikeza umbala obomvu kumashubhu ezithombe ze-TV ezinombala.
4: I-Yttrium Oxide isetshenziswa futhi ekwenzeni i-Yttrium-Iron-Garnets, okuyizihlungi ze-microwave ezisebenza kahle kakhulu.
| ITEM | IZINHLOBO | IMIPHUMELA YOKUHLOLA | ||||||
| Y2O3/TREO(%,min) | 99.995 | 99.999 | ||||||
| I-TREO(%,min) | 98 | 98.38 | ||||||
| Usayizi Wezinhlayiya | 30-60nm, 1.0-2.0um, 0.3-0.6um, 0.6-1.0um | Ukuvumelana | ||||||
| Ukungcola kwe-RE(/REO,%) | ||||||||
| I-La2O3 | ≤0.0005 | ≤0.0001 | ||||||
| I-CeO2 | ≤0.0005 | ≤0.0001 | ||||||
| I-Pr6O11 | ≤0.0002 | ≤0.0001 | ||||||
| Nd2O3 | ≤0.0002 | ≤0.0001 | ||||||
| I-Sm2O3 | ≤0.0002 | ≤0.0001 | ||||||
| I-Eu2O3 | ≤0.0002 | ≤0.0001 | ||||||
| I-Gd2O3 | ≤0.0002 | ≤0.0001 | ||||||
| I-Tb4O7 | ≤0.0002 | ≤0.0001 | ||||||
| I-Dy2O3 | ≤0.0002 | ≤0.0001 | ||||||
| I-Ho2O3 | ≤0.001 | ≤0.0001 | ||||||
| I-Er2O3 | ≤0.001 | ≤0.0001 | ||||||
| I-Tm2O3 | ≤0.0001 | ≤0.00002 | ||||||
| Yb2O3 | ≤0.0001 | ≤0.00002 | ||||||
| I-Lu2O3 | ≤0.0001 | ≤0.00002 | ||||||
| I-LOI | ≤2% | |||||||